The oxidative stabilization and carbonization of a synthetic mesophase pitch, part I: The oxidative stabilization process
Drbohlav, J. Stevenson, William T.K.
Drbohlav, J.
Stevenson, William T.K.
Citations
Altmetric:
Authors
Other Names
Location
Time Period
Advisors
Original Date
Digitization Date
Issue Date
1995
Type
Article
Genre
Keywords
FT-IR,Mechanisms,Mesophase pitch,Naphthenic rings,Oxidation
Subjects (LCSH)
Citation
Drbohlav, J. & Stevenson, W.T.K.. (1995). The oxidative stabilization and carbonization of a synthetic mesophase pitch, part I: The oxidative stabilization process. Carbon. 33. 693-711. 10.1016/0008-6223(95)00011-2.
Abstract
The transformation of mesophase pitch to an ordered carbon by high-temperature heat treatment in an inert atmosphere must be preceded by a suitable period of thermosetting or oxidative stabilization. The chemical process of oxidative stabilization is not well characterized, although research has clearly indicated that the oxidation history of the mesophase has a profound impact on the mechanical qualities of the resultant carbon product. In this study, we oxidized samples of a commercially available, synthetic mesophase pitch to determine the effect of different time/temperature profiles of oxidation on the quantity and type of introduced functionality. Fourier transform infrared spectroscopy (FT-IR) was used to characterize and quantify oxygen functionality present in this oxidized pitch. The oxidation process was characterized by periods of weight gain and weight loss. It was concluded that weight gain during oxidation involves the loss of aliphatic content in the pitch, with a concurrent increase in oxygen content as predominately ester and anhydride functionality. Weight loss is characterized by a loss of aromatic carbon content from the pitch and a further increase in the relative oxygen content in the pitch. It was discovered that changing the time/temperature profile of oxidation affects the pitch primarily via the degree of weight gain and weight loss experienced, rather than through the introduction of specific functionality with weight gain dominating at lower oxidation temperatures and shorter time periods, and weight loss dominating at higher temperatures and longer periods of oxidation. We conclude by suggesting mechanisms of derivatization to explain the oxidative stabilization of this synthetic, naphthalene-derived mesophase pitch in an oxygen-rich atmosphere. © 1995.
Table of Contents
Description
This is an open access article under the CC by license
Publisher
Elsevier Ltd
Journal
Carbon
Book Title
Series
Digital Collection
Finding Aid URL
Use and Reproduction
Archival Collection
PubMed ID
ISSN
0008-6223